Hempel High Protect Two-component Primer A+B Primer 2,5Lt Cream 456COL038
Visit us in our shop
WE ARE AT YOUR DISPOSAL AT OUR POINT OF SALE
Not just online! Come and visit us also in the shop!
In our store you will find a wide selection of selected items and you will be assisted by our specialized staff with over a decade of experience in the nautical sector.
Everything for the boat ... deck equipment, anchoring and mooring, hydraulic and electrical systems, photovoltaics, stainless steel hardware, antifouling and paints, engine spare parts, on-board safety, sailing accessories, nautical instruments, GPS, depth sounders and much more!
We are in San Giorgio di Nogaro in the province of Udine, an important basin, located in the Bassa Friulana, bathed by the Corno river ... a few km from well-known destinations such as Lignano, Grado, Trieste etc.
Nautimarket Europe s.r.l., Via Marittima 17, 33058 San Giorgio di Nogaro (UD) Italy
(modificale nel modulo Rassicurazioni cliente)
(modificale nel modulo Rassicurazioni cliente)
(modificale nel modulo Rassicurazioni cliente)
MORE INFORMATION
Unit size 2.5Lt. Cream.
HIGH PROTECT A + B PRIMER
PHYSICAL CONSTANTS:
Finish: High gloss
Volume solids,% 100
Theoretical coverage: 2.9 m2 / l [116.3 sq.ft. / US gallon] - 350 micron / 14 mils
Flash point: 74 ° C [165.2 ° F]
Specific weight: 1.3 kg / liter [10.5 lb / US gallons]
Touch dry: 10-12 hour (s) 20°C / 68°F, 22 to 27 hours at 10°C / 50°F
Fully cured: 7 days (i) 20°C / 68°F, 14 days (i) at 10°C / 50 ° F
VOC content: 10 g / l [0.1 lb / US gallons]
APPLICATION DETAILS:
Mixing ratio: 3: 2 by volume
Application method: Airless / brush / sponge roller
Thinner, (volume max): Do not dilute
Pot life: 45 minutes (i) 20°C / 68°F, 60 minutes at 15°C / 59°F
Hole nozzle: 0.023 "
Nozzle pressure: 250 bar [3625 psi] (Airless spray data are indicative and subject to adjustment)
Cleaning equipment: HEMPEL'S THINNER 08451 The roller is discarded after use.
Dry thickness indicated 350 micron [14 mils]
Thick wet indicated 350 micron [14 mils]
Recoat interval, min to specification.
Recoat interval, max As per specification.
SURFACE PREPARATION:
Wash the area to be treated with HEMPEL'S PRE-CLEAN 67602 as set out in the instructions and rinse with fresh water. Remove salt and other contaminants by cleaning with fresh water at high pressure.
Fibreglass: The surface should be abraded with to uniform roughness (sandpaper, grit 80-100). Remove any dust.
Steel: Sand to Sa 2½, ISO 8501-1: 2007, surface profile corresponding to Rugotest No. 3, BN 11.
PRODUCT APPLICATION:
Use only where application and curing take place at temperatures higher than 10°C / 50°F. The temperature of the paint must be equal to 15°C or higher. When applying, the surface must be perfectly clean, dry and temperature must be above the dew point to prevent the formation of condensation.
Fibreglass: For osmosis repairs, apply at least 2 layers with dry film thickness of 350 microns each (at least 4 layers with dry film thickness of 150 microns each for roller applications). For preventive treatments, apply at least one layer with a dry film thickness of 350 microns each (at least 2 layers with dry film thickness of 150 microns each for roller applications).
Steel: minimum 3 layers of 150 micron / 6 mils dry film thickness each.
Application equipment
We recommend using ½ '' hoses between the pump and the spray gun to avoid pressure drops and, if possible, remove the suction hose.
Film thickness / dilution
A different thickness may be specified, depending on use and area of use. This will alter coverage. For roller application, it is essential to ensure that the layer of the specified film is not porous.
Catalyst
The catalyst is highly thixotropic. Add 3 basic parts to 2 parts of catalyst during stirring.
Undocking
The boat should not be put back in the water prior to one week from catalysis of the last layer of the product (20°C). 2 weeks at 10°C / 50°F.
Overcoating
If the interval is exceeded, it will be necessary to apply a thin coat of HEMPEL'S LIGHT PRIMER 45551. After prolonged exposure to the elements, before recoating completely clean the surface using high-pressure cleaning with fresh water and allow to dry.